Entwicklung halogenfrei flammgeschützter Polyamide

Klitsch, Johannes (2023)
Entwicklung halogenfrei flammgeschützter Polyamide.
Technische Universität Darmstadt
doi: 10.26083/tuprints-00024062
Ph.D. Thesis, Primary publication, Publisher's Version

Text
Dissertation- Johannes Klitsch.pdf
Copyright Information: CC BY-NC-ND 4.0 International - Creative Commons, Attribution NonCommercial, NoDerivs.
Download (5MB)

Item Type:

Ph.D. Thesis

Type of entry:

Primary publication

Title:

Entwicklung halogenfrei flammgeschützter Polyamide

Language:

German

Referees:

Rehahn, Prof. Dr. Matthias ; Pfaendner, Prof. Dr. Rudolf

Date:

2023

Place of Publication:

Darmstadt

Collation:

ix, 145 Seiten

Date of oral examination:

22 May 2023

DOI:

10.26083/tuprints-00024062

Abstract:

Im Rahmen dieser Arbeit wurden halogenfreie Flammschutzmittelkonzepte für glasfaserverstärktes PA 66 entwickelt und im Hinblick auf Ihre Wirkweise in Gas- und Festphase untersucht. Basierend auf der Verwendung von Zn-DOPOx wurden dabei durch Kombination mit geeigneten Co-Flammschutzmitteln neuartige halogenfreie Systeme entwickelt. Tiefergehend wurde dabei im ersten Teil erstmals die Wirkweisen von Zn-DOPOx sowie der Kombination aus Zn-DOPOx mit MPP näher analysiert. Anhand der Ergebnisse des UL-94 V Brandtests zeigte sich ein stark ausgeprägter Synergismus bei einem Gewichtsverhältnis von 1:1. Durch die Kopplung mit der Cone-Calorimetrie sowie ergänzenden Analysemethoden (DTA-TGA-MS-FTIR, REM-EDX, ATR-FTIR) konnte der Ursprung des synergistischen Effekts besonders auf Beiträge in der Gasphase zurückgeführt werden. Im zweiten Teil wurde der Effekt der Zugabe von DEPAl bzw. DEPZn zu Zn-DOPOx:MPP näher untersucht. Besonders im Fokus stand dabei die Untersuchung der unterschiedlichen Wirkung der beiden Diethylphosphinsäuresalze in den ternären Abmischungen in Gas- und Festphase.

Alternative Abstract:

Alternative Abstract

Language

In this work, halogen-free flame retardant concepts were developed for glass fiber reinforced PA 66 and investigated for their mode of action in the gas and condensed phases. Based on the use of Zn-DOPOx in combination with suitable co-flame retardants, novel halogen-free systems were developed. In the first part, the modes of action of Zn-DOPOx and the combination of Zn-DOPOx with MPP were analyzed in more detail for the first time. Based on the results of the UL-94 V test, a strong synergistic effect using a weight ratio of 1:1 was identified. With the use of the cone calorimetry as well as complementary analytical methods (DTA-TGA-MS-FTIR, SEM-EDX, ATR-FTIR), the origin of the synergistic effect could be traced back to especially contributions in the gas phase. In the second part, the effect of the addition of DEPAl or DEPZn to Zn-DOPOx:MPP was investigated in more detail. Special focus was given to the investigation of the different effects of the two diethylphosphinic acid salts in the ternary mixtures in gas and solid phase.

English

Status:

Publisher's Version

URN:

urn:nbn:de:tuda-tuprints-240629

Classification DDC:

500 Science and mathematics > 540 Chemistry