Farben von Titanaten des Freudenbergit-Strukturtyps

Bruhn, Gerd (2012)
Farben von Titanaten des Freudenbergit-Strukturtyps.
Technische Universität Darmstadt
Ph.D. Thesis, Primary publication

[img]
Preview
Text
Gerd-Bruhn-dissertation-tuprints.pdf
Copyright Information: CC BY-NC-ND 2.5 Generic - Creative Commons, Attribution, NonCommercial, NoDerivs .

Download (13MB) | Preview
Item Type: Ph.D. Thesis
Type of entry: Primary publication
Title: Farben von Titanaten des Freudenbergit-Strukturtyps
Language: German
Referees: Albert, Prof. Dr. Babara ; Pfaff, Prof. Dr. Gerhard
Date: 13 December 2012
Place of Publication: Darmstadt
Date of oral examination: 10 December 2012
Abstract:

Es wurden Natriumtitanate des Freudenbergit-Strukturtyps Na2MxTi8-xO16 (M = Fe, Zn, Ni, Co, Mn) synthetisiert. Das nur Eisen enthaltende Natriumtitanat wurde bezüglich der Kristallisationstemperatur und Stabilität in oxidierender und reduzierender Atmosphäre untersucht. Phasenreine Natriumtitanate des Freudenbergit-Strukturtyps mit Zn, Ni, Co und Mn wurden zum ersten Mal erhalten und beschrieben. Die Rietveld-Verfeinerungen der Kristallstrukturen wurde auf Basis von Synchrotron- und Röntgenpulverdiffraktogrammen vorgenommen und lieferte unter anderem Aussagen zur statistischen Teilbesetzung der Titanatom-Positionen mit anderen Metallatomen (Fe, Zn, Ni, Co, Mn). Einige der untersuchten Natriumtitanate des Freudenbergit-Strukturtyps sind farbig und wurden auf ihre Eignung als Pigmente geprüft. Sie wurden mit der Methode der diffusen Reflexion untersucht, um Absorptionsspektren zu erhalten. Von den Pigmentpulvern wurden Lackkarten angefertigt. Die CIE L*a*b*-Werte wurden ermittelt und mit bekannten Pigmenten, die den gleichen Chromophor enthalten, verglichen.

Alternative Abstract:
Alternative AbstractLanguage

Sodium titanates of the Freudenbergite structure type Na2MxTi8-xO16 (M=Fe, Zn, Ni, Co, Mn) were synthesized. The iron-containing sodium titanate was characterized for its crystallization temperature and the stability in oxidizing and reducing atmosphere. For the first time phase pure sodium titanates of the Freudenbergite structure type containing Zn, Ni, Co and Mn were obtained and described. Rietveld-refinement of the crystal structure from synchrotron and X-ray powder data resulted among others in good fits for the statistically occupation of the titanium atom position with other metal atoms (Fe, Zn, Ni, Co, Mn). Some of the sodium titanates of the Freudenbergite structure type are colored and were investigated for the capability as pigments. These were measured with diffuse reflectance to get absorption spectra. With the colored pigment powders lacquer cards were prepared. The CIE L*a*b*-values were measured and compared with known pigments with the same chromophore.

English
Uncontrolled Keywords: Freudenbergit, diffuse Reflexion, Rietveld Verfeinerung, Pigment, CIE L*a*b*
Alternative keywords:
Alternative keywordsLanguage
Freudenbergite, diffuse reflectance, rietveld refinement, pigment, CIE L*a*b*English
URN: urn:nbn:de:tuda-tuprints-32728
Classification DDC: 500 Science and mathematics > 500 Science
500 Science and mathematics > 540 Chemistry
Divisions: 07 Department of Chemistry
07 Department of Chemistry > Eduard Zintl-Institut > Fachgebiet Anorganische Chemie
Date Deposited: 31 Jan 2013 09:05
Last Modified: 09 Jul 2020 00:16
URI: https://tuprints.ulb.tu-darmstadt.de/id/eprint/3272
PPN: 386298890
Export:
Actions (login required)
View Item View Item