Synthese und Charakterisierung von Spinell-Sialon

Groß, Toni André (2012)
Synthese und Charakterisierung von Spinell-Sialon.
Technische Universität Darmstadt
Ph.D. Thesis, Primary publication

[img]
Preview
PDF
Dissertation.pdf
Copyright Information: CC BY-NC-ND 2.5 Generic - Creative Commons, Attribution, NonCommercial, NoDerivs .

Download (27MB) | Preview
Item Type: Ph.D. Thesis
Type of entry: Primary publication
Title: Synthese und Charakterisierung von Spinell-Sialon
Language: German
Referees: Fueß, Prof. Dr.- Hartmut ; Riedel, Prof. Dr. Ralf
Date: 20 February 2012
Place of Publication: Darmstadt
Date of oral examination: 18 October 2011
Abstract:

Im Rahmen der vorliegenden Arbeit wurden Synthesebedingungen sowie grundlegende Materialeigenschaften der Hochdruckmodifikation von Sialon (Spinell-Sialon) untersucht. Durch eine Phasenanalyse der Produkte bei den Hochdruck- und Hochtemperatursynthesen konnten einige Faktoren identifiziert werden, welche einen möglichst hohen Grad der Umwandlung von beta- in gamma-Sialon begünstigen. Durch die Anwendung der Rietveld-Methode konnte aus Röntgenpulverdiffraktogrammen bei unterschiedlichen Temperaturen der temperaturabhängige Ausdehnungskoeffizient einer Zusammensetzung von Spinell-Sialon (x = 2,1) im Temperaturbereich von 20-1220 °C bestimmt werden. Mit einer Kombination von Vickers- und Knoopeindrücken sowie einer Messung der Kompressibilität (für die Zusammensetzung x = 2,1) konnten einige mechanische Kennwerte ermittelt werden, darunter die lastunabhängige Härte in Abhängigkeit der Zusammensetzung, der Elastizitätsmodul – ebenfalls in Abhängigkeit von der Zusammensetzung – und weiterhin Kompressionsmodul, Schubmodul und Querkontraktionszahl, jeweils für die Zusammensetzung, bei der die Kompressibilitätsmessungen durchgeführt wurden. Über kombinierte NEXAFS- und SXFS-Messungen wurde die elektronische Struktur nahe der Fermikante von beta- in gamma-Sialon in Abhängigkeit von der Zusammensetzung dargestellt; vermittels dieser Werte wiederum konnten die elektronischen Bandlücken dieser Zusammensetzungen abgeschätzt werden.

Alternative Abstract:
Alternative AbstractLanguage

This work examined the conditions for synthesis as well as basic material properties of the high pressure modification of Sialon (spinel-Sialon). Phase analysis of the products of high-pressure and high-temperature syntheses resulted in better understanding of the conditions needed for a successful beta to gamma transformation. Rietveld-analysis of diffractograms taken at different temperatures yielded in the temperature-dependent coefficient of thermal expansion for the composition x = 2,1 in the temperature range 20-1220°C. Combination of Vickers and Knoop hardness measurements along with a measurement of the compressibility of a particular composition (x = 2,1) have been used to determine some mechanical properties, mostly in dependency of the composition. Among the properties were load-independent hardness, Young’s modulus, bulk modulus, shear modulus and Poisson ratio (the latter three for the composition, which has been used for the compressibility mesurements). A combination of NEXAFS- und SXFS-measurements revealed the electronic structure near the Fermi level for different compositions of beta- and gamma-Sialons. Those measurements were used to approximate the electronic bandgap of those compositions.

English
Alternative keywords:
Alternative keywordsLanguage
Hochdruck, Multi-Anvil, Spinell-SialonGerman
high pressure, multi-anvil, spinel-sialonEnglish
URN: urn:nbn:de:tuda-tuprints-29039
Classification DDC: 600 Technology, medicine, applied sciences > 620 Engineering and machine engineering
Divisions: 11 Department of Materials and Earth Sciences > Material Science
11 Department of Materials and Earth Sciences > Material Science > Structure Research
Date Deposited: 02 Mar 2012 08:13
Last Modified: 09 Jul 2020 00:02
URI: https://tuprints.ulb.tu-darmstadt.de/id/eprint/2903
PPN: 386255393
Export:
Actions (login required)
View Item View Item