TU Darmstadt / ULB / TUprints

Elektron-dotierte Kuprate und Rhenate

Winkler, Andreas (2008)
Elektron-dotierte Kuprate und Rhenate.
Technische Universität Darmstadt
Ph.D. Thesis, Primary publication

[img]
Preview
PDF
Thesis.pdf
Copyright Information: In Copyright.

Download (11MB) | Preview
Item Type: Ph.D. Thesis
Type of entry: Primary publication
Title: Elektron-dotierte Kuprate und Rhenate
Language: German
Referees: Alff, Prof. Dr. Lambert ; Donner, Prof. Dr. Wolfgang
Date: 19 December 2008
Place of Publication: Darmstadt
Date of oral examination: 16 December 2008
Abstract:

Es wurden mittels MBE supraleitende elektrondotierte Kuprat-Schichten La2-xCexCuO4 und nominell undotierte Kuprat-Schichten LaYCuO4 hergestellt. Mittels Vier-Punkt-Messung wurde der temperaturabhängige spezifische Widerstand gemessen und der spezifische Widerstand bei Raumtemperatur und beim Einsetzen der Supraleitung sowie die kritische Temperatur bestimmt. Im Phasendiagramm wird weiterhin die Kristallinität der Proben aufgenommen. Myon-Spin-Rotations Messungen zeigen eine magnetische an der Oberfläche der dünnen Schichten. Weiterhin werden XMCD-Messungen am System der ferromagnetischen Doppelperowskiten Ca2FeReO6, Sr2FeReO6 und Ba2FeReO6 gezeigt. Ca2FeReO6 zeigt ein dahingehend unerwartetes Verhalten wie es die höchste Curietemperatur des Trios aufweist.

Alternative Abstract:
Alternative AbstractLanguage

Superconducting electron doped cuprate thin films La2-xCexCuO4 and nominally undoped cuprate thin films LaYCuO4 were synthesized by MBE. By four point measurement the temperature dependent resistivity was determined. Also resisitivity at room-temperatur and at onset of supercondictivity were determined. The phase diagram was amended by the cristallinity of the samples. Myon-Spin-Rotation measurements show a magnetic layer at the surface of the thin films. Further XMCD-measurements on the ferromagnetic double pervskites Ca2FeReO6, Sr2FeReO6 and Ba2FeReO6 are shown. Ca2FeReO6 shows unexpected behaviour as it comprises the highest Curie-temperatur among the three compounds.

English
Uncontrolled Keywords: electron-doped LCCO La2-xCexCuO4 Ba2FeReO6 Sr2FeReO6 Ca2FeReO6 XMCD double perovskites
Alternative keywords:
Alternative keywordsLanguage
electron-doped LCCO La2-xCexCuO4 Ba2FeReO6 Sr2FeReO6 Ca2FeReO6 XMCD double perovskitesEnglish
URN: urn:nbn:de:tuda-tuprints-12226
Classification DDC: 500 Science and mathematics > 500 Science
500 Science and mathematics > 530 Physics
Divisions: 11 Department of Materials and Earth Sciences
Date Deposited: 20 Jan 2009 12:05
Last Modified: 08 Jul 2020 23:15
URI: https://tuprints.ulb.tu-darmstadt.de/id/eprint/1222
PPN: 208323872
Export:
Actions (login required)
View Item View Item