Manganoxide als Katalysator für die alkalische Sauerstoffentwicklungsreaktion

Connor, Paula (2020)
Manganoxide als Katalysator für die alkalische Sauerstoffentwicklungsreaktion.
Technische Universität Darmstadt
doi: 10.25534/tuprints-00011914
Ph.D. Thesis, Primary publication

[img]
Preview
Text
Promo_Paula_Connor_pub.pdf
Copyright Information: CC BY-NC-SA 4.0 International - Creative Commons, Attribution NonCommercial, ShareAlike.

Download (15MB) | Preview
Item Type: Ph.D. Thesis
Type of entry: Primary publication
Title: Manganoxide als Katalysator für die alkalische Sauerstoffentwicklungsreaktion
Language: German
Referees: Jaegermann, Prof. Dr. Wolfram ; Kramm, Prof. Dr. Ulrike
Date: 2020
Place of Publication: Darmstadt
Date of oral examination: 23 June 2020
DOI: 10.25534/tuprints-00011914
Abstract:

Mangan spielt eine Schlüsselrolle in der Natur bei der Sauerstoffentwicklungsreaktion im Photosystem II. Durch diese Rolle stieg das Forschungsinteresse an Manganoxiden als Katalysator in den letzten Dekaden. In dieser Arbeit wurden zwei unterschiedliche Manganoxide (MnO und MnO2) für den Einsatz als Katalysator für die Sauerstoffentwicklungsreaktion untersucht. Dabei lag der Fokus vor allem auf den Veränderungen an der Katalysatoroberfläche während der elektrochemischen Messungen und auf der Anpassung des Manganoxides an das darunterliegende Substrat. Für diese Untersuchungen wurden dünne Schichten mittels reaktiver Kathodenzerstäubung auf unterschiedlichen Substraten präpariert und anschließend mittels XPS, Raman und EIS Messungen analysiert.

Alternative Abstract:
Alternative AbstractLanguage

Manganese plays a key role for the oxygen evolution reaction in the photosystem II in the nature. Therefore, research activities on manganese oxide as catalyst increased in the last decades. In this work two different manganese oxides (MnO and MnO2) were investigated as catalyst for the oxygen evolution reaction in alkaline solution. Here, changes of the catalyst surface during electrochemical measurements were investigated as well as the adaption of the manganese oxide catalyst with respect to the underlaying substrate. For these investigations, thin films were prepared with a reactive sputtering process on different substrates and afterwards characterized by XPS, Raman and EIS measurements.

English
URN: urn:nbn:de:tuda-tuprints-119142
Classification DDC: 500 Science and mathematics > 500 Science
500 Science and mathematics > 540 Chemistry
Divisions: 11 Department of Materials and Earth Sciences > Material Science > Surface Science
Date Deposited: 10 Aug 2020 13:23
Last Modified: 10 Aug 2020 13:35
URI: https://tuprints.ulb.tu-darmstadt.de/id/eprint/11914
PPN: 467930872
Export:
Actions (login required)
View Item View Item