Deposition, Charakterisierung und Bandanpassung oxidischer Dünnschichtmaterialien zur Lichtabsorption

Morasch, Jan :
Deposition, Charakterisierung und Bandanpassung oxidischer Dünnschichtmaterialien zur Lichtabsorption.
Technische Universität, Darmstadt
[Ph.D. Thesis], (2017)

[img]
Preview
Dissertation Jan Morasch Druckversion - Text (A4)
Dissertation Jan Morasch Druckversion.pdf - Accepted Version
Available under CC-BY-NC-ND 4.0 International - Creative Commons Attribution Non-commercial No-derivatives 4.0.

Download (6MB) | Preview
Item Type: Ph.D. Thesis
Title: Deposition, Charakterisierung und Bandanpassung oxidischer Dünnschichtmaterialien zur Lichtabsorption
Language: German
Abstract:

Diese Dissertation ist im Rahmen des All-Oxide Photovoltaik Projekts entstanden, welches die Entwicklung einer vollständig oxidischen Solarzelle zum Ziel hatte. Die vorliegende Arbeit beschäftigt sich daher mit der Herstellung und Charakterisierung von oxidischen Dünnschichtmaterialien zur Lichtabsorption. Die Deposition der Schichten erfolgte mittels reaktiver (Ko-)Magnetron-Kathodenzerstäubung. Eine Charakterisierung der Proben erfolgte unter anderem mit Hilfe von Photoelektronenspektroskopie (XPS/UPS) und UV/VIS/NIR-Transmissionsspektroskopie. Die elektronischen Eigenschaften und das Absorptionsverhalten konnten dadurch in Abhängigkeit der Schichtzusammensetzung untersucht werden. Des Weiteren wurden Grenzflächenuntersuchungen zu potentiellen Kontaktmaterialien durchgeführt sowie Solarzellen im Labormaßstab hergestellt. Dadurch konnten sowohl Erkenntnisse über die Transitivität von Übergangsmetalloxiden als auch über den Einfluss von Fermi-Niveau-Pinning auf die offene Klemmspannung von Solarzellen gewonnen werden.

Alternative Abstract:
Alternative AbstractLanguage
This dissertation emerged in the framework of the All-Oxide Photovoltaic project, which had the development of a completely oxidic solar cell as a main goal. The present thesis deals with the preparation and characterization of oxidic thin films for light absorption. The samples were deposited via reactive (co-)magnetron sputtering. Photoelectron Spectroscopy (XPS/UPS) and UV/VIS/NIR-Transmission Spectroscopy were used as the main characterization methods. The electronic properties and the absorption behavior were investigated with respect to the film composition. In addition the interfaces to potential contact materials were studied and laboratory scaled solar cells were built. This gave insight into the transitivity of transition metal oxides as well as into the influence of Fermi-level-pinning on the open circuit voltage of solar cells.English
Place of Publication: Darmstadt
Classification DDC: 500 Naturwissenschaften und Mathematik > 500 Naturwissenschaften
500 Naturwissenschaften und Mathematik > 530 Physik
600 Technik, Medizin, angewandte Wissenschaften > 600 Technik
Divisions: 11 Department of Materials and Earth Sciences > Material Science
11 Department of Materials and Earth Sciences > Material Science > Surface Science
Date Deposited: 09 Oct 2017 07:43
Last Modified: 09 Oct 2017 07:43
URN: urn:nbn:de:tuda-tuprints-67994
Referees: Klein, Prof. Dr. Andreas and Ensinger, Prof. Dr. Wolfgang
Refereed: 6 September 2017
URI: http://tuprints.ulb.tu-darmstadt.de/id/eprint/6799
Export:
Actions (login required)
View Item View Item

Downloads

Downloads per month over past year