Suzuki-Polykondensation hochmolekularer Poly-para-phenylene mittels Mikrowellenstrahlung

von Irmer, Jonas (2021)
Suzuki-Polykondensation hochmolekularer Poly-para-phenylene mittels Mikrowellenstrahlung.
Technische Universität Darmstadt
doi: 10.26083/tuprints-00011876
Ph.D. Thesis, Primary publication, Publisher's Version

[img]
Preview
Text
Dissertation_Jonas_von_Irmer.pdf
Copyright Information: CC BY-NC-ND 4.0 International - Creative Commons, Attribution NonCommercial, NoDerivs.

Download (6MB) | Preview
Item Type: Ph.D. Thesis
Type of entry: Primary publication
Title: Suzuki-Polykondensation hochmolekularer Poly-para-phenylene mittels Mikrowellenstrahlung
Language: German
Referees: Rehahn, Prof. Dr. Matthias ; Thiele, Prof. Dr. Christina M.
Date: 2021
Place of Publication: Darmstadt
Collation: i, 136, XIII, c Seiten
Date of oral examination: 9 November 2020
DOI: 10.26083/tuprints-00011876
Abstract:

Die Suzuki-Polykondensation (SPC) von Poly-para-phenylenen (PPP) wird durch ein besonders zeiteffizientes Syntheseprotokoll unter Verwendung von Mikrowellen-Erwärmung weiterentwickelt. Mehrzähnige Dendrimer- sowie Polymer-basierte Phosphin-Palladium-Komplexe werden entwickelt und als Katalysatoren in der Mikrowellen-SPC eingesetzt, um ein Kettenwachstumsmechanismus zu induzieren. Erstmals wird die Katalysatortransfer Polymerisation (CTP) unter Mikrowellen-Erwärmung durchgeführt und liefert dabei besonders hochmolekulare Produkte, welche mittels MALDI-TOF untersucht werden, um das Ablaufen nach einem Kettenwachstums-Mechanismus zu beweisen.

Alternative Abstract:
Alternative AbstractLanguage

The Suzuki-polycondensation (SPC) of poly-para-phenylenes (PPP) is improved by applying a time-efficient microwave-assisted synthetic protocol. Multidentate dendrimer- and polymer-based phosphine-palladium-complexes are developed and used as a catalyst in the microwave-SPC to induce a chaingrowth mechanism. For the first time, a catalyst transfer polymerization (CTP) is conducted under microwave irradiation and leads to high molecular weight polymers which are characterized via MALDI-TOF to confirm the undelying chain-growth mechanism.

English
Status: Publisher's Version
URN: urn:nbn:de:tuda-tuprints-118767
Classification DDC: 500 Science and mathematics > 540 Chemistry
Divisions: 07 Department of Chemistry > Ernst-Berl-Institut > Fachgebiet Makromolekulare Chemie
Date Deposited: 22 Feb 2021 13:56
Last Modified: 22 Feb 2021 13:56
URI: https://tuprints.ulb.tu-darmstadt.de/id/eprint/11876
PPN: 476597560
Export:
Actions (login required)
View Item View Item